耐蝕合金GB/T15012 Inconel600冷軋帶生產(chǎn)標準
耐蝕合金冷軋帶生產(chǎn)標準 GB／T15012—1994
耐熱合金冷軋帶的尺寸規(guī)格 (mm)
|
厚度及
厚度允
許偏差
|
寬度
厚度
|
厚度允許偏差
|
|
20～150
|
>150～250
|
>250～400
|
>400～630
|
|
0.02～O.10
|
±O.008
|
±O.010
|
±O.OlO
|
|
|
>0.10～0.15
|
±0.010
|
±0.010
|
±O.OlO
|
|
|
>O.15～O.25
|
±O.015
|
±0.015
|
±O.015
|
±0.020
|
|
>O.25～O.45
|
±O.020
|
±0.020
|
±O.020
|
±O.025
|
|
>O.45～0.65
|
±O.O25
|
±0.025
|
±0.025
|
±O.030
|
|
>O.65～O.90
|
±O.030
|
±0.030
|
±0.030
|
±0.040
|
|
>0.90～1.20
|
±0.035
|
±O.040
|
±O.040
|
±O.045
|
|
>1.20～1.50
|
±O.045
|
±O.050
|
±O.050
|
±O.055
|
|
>1.50～1.80
|
±0.06
|
±0.065
|
±0.065
|
±O.07
|
|
>1.80～2.00
|
±O.06
|
±0.07
|
±0.075
|
±O.08
|
|
>2.00～2.30
|
±O.07
|
士O.08
|
±0.08
|
士0.09
|
|
>2.30～2.50
|
±O.07
|
土O.08
|
±0.08
|
±0.09
|
|
>2.50～3.10
|
±O.08
|
±O.09
|
±O.09
|
±O.10
|
|
>3.10～4.00
|
±O.09
|
±O.10
|
±O.10
|
±0.11
|
|
寬度及寬度允
許偏差
|
寬度邊緣狀態(tài)
|
寬度允許偏差
|
|
20～50
|
>50～150
|
>150～250
|
>250～400
|
>400～630
|
|
切邊帶材
|
+l.O
O
|
+2.O
O
|
+3.0
0
|
+4.0
0
|
+5.0
0
|
|
不切邊帶材
|
+2
-l
|
+3
-2
|
+6
-2
|
+7
-3
|
+20
O
|
注：1.切邊帶材的鐮刀彎應(yīng)符合下列規(guī)定：
寬度20—50mm帶材，每米長度不大于3mm；寬度大于50mm帶材，每米長度不大于2mm。
2.根據(jù)需方要求，可以把表中厚度的正負偏差改為正偏差或負偏差，但此時的公差值應(yīng)與表中規(guī)定的公差值相等。
耐蝕合金冷軋帶的力學性能
|
合**號
|
狀態(tài)
|
抗拉強度ób／MPa
|
屈服強度ó0.2／MPa
|
伸長率δ5(％)
|
硬度
|
|
≥
|
|
NS111
NS112
|
退火
|
520
|
205
|
30
|
—
|
|
NS142
|
退火
|
585
|
240
|
30
|
≤95HRB
|
|
NS311
|
固溶
|
570
|
245
|
45
|
—
|
|
1／2H
|
805
|
—
|
10
|
—
|
|
NS312
NS315
|
退火
|
505
|
240
|
30
|
—
|
|
1／4H
|
—
|
—
|
—
|
88～94HRB
|
|
1／2H
|
—
|
—
|
—
|
93～98HRB
|
|
3／4H
|
—
|
—
|
—
|
97HRB～25HRC
|
|
H
|
860
|
620
|
2
|
—
|
|
NS321
|
退火
|
795
|
345
|
45
|
100HRB①
|
|
NS322
|
退火
|
760
|
350
|
40
|
100HRB①
|
|
NS333
|
固溶
|
690
|
315
|
30
|
—
|
|
NS336
|
退火
|
830
|
415
|
30
|
—
|
|
固溶
|
690
|
275
|
30
|
—
|
GB/T15012 Inconel 耐蝕合金冷軋帶生產(chǎn)標準
注：1.屈服強度值，僅當需方要求時(在合同中注明)才測定。
2.屈服強度要求不適用于厚度小于0.50mm的帶材。
3.厚度小于0.25mm的帶材不作拉力試驗，但應(yīng)提供硬度數(shù)據(jù)。
①硬度值僅供參考。
GB/T15012 Inconel 耐蝕合金冷軋帶生產(chǎn)標準